Features
Lasting color
Excellent anti-load Capacity
Good Sound Insulation
Excellent Corrosion Resistance
Good shock Resistance
Low Temperature Resistance
Excellent Self-cleaning
Excellent Heat Insulation
Volume Stability
Excellent Water Resistance
Strong Fire Retardant
Excellent Insulation
Environment Protection
Rapid Installation
ASA Roof Sheet Project
ASA Resin Roof Sheet Project
Synthetic Resin Roof Sheet Project
Synthetic Resin Roof Project
| NO. | Test item | Test method |
| 1 | Color persistence | ISO4892-2:2013,ISO105-A02:199 3 Cor2:2005 and ASTM D2244-11 |
| 2 | Muriatic acid resistance | ISO175-2010 |
| 3 | Sulfuric acid resistance | ISO175-2010 |
| 4 | Alkali resistance | ISO175-2010 |
| 5 | Tensile strength | ISO 527-1:2012 and ISO527-2:2012 |
| 6 | Nominal tensile strain at break | ISO 527-1:2012 and ISO527-2:2012 |
| 7 | Flexural strength | ISO 178:2010 / Amd.1:2013Method A |
| 8 | Impact resistance | GB/T 8814-2004 Section5.7 and 6.7 |
| 9 | Oxygen Index | ISO 4589-1:1996 and ISO4589-2:1996 / Amd.1:2005 |
| 10 | Burning test | DIN 4102-1:1998-05 |
ASA SYNTHETIC RESIN ROOF TILE TEST RESULT FROM SGS (2014)
| NO. | Test item | Test method | Test condition |
| 1 | Xenon-arc Exposure | ISO 4892-2:2013,ISO 105-A02:1993 Cor2: 2005 and ASTM D2244-11 | ISO 4892-2:2013 cycle 4 Irradiance:(0.51±0.02)W/(m2·nm)@340nm 102min light at (63±3)℃BPT,(50±10)℃RH 18min light and water sparay Filter: Boro / Boro Exposure period: 500h |
| 2 | Thermal resistance | With reference to ASTM D3045-92(2010) and client’s requirements | 150℃.30min |
| 3 | Muriatic acid resistance | With reference to ISO 175-2010 and client’s requirements | Medium: 35%(m/m) HCI(AR) Method: Immersion method Temperature: Room temperature Test time: 48h |
| 4 | Sulfuric acid resistance | With reference to ISO 175-2010 and client’s requirements | Medium: 30%(m/m) H2SO4(AR) |
| 5 | Alikali resistance | With reference to ISO 175-2010 and client’s requirements | Medium: 40% (m/m) NaOH(AR) Method: Immersion method Temperature: Room temperature Test time: 48h |
| 6 | Density | ISO 1183-1:2012 Method A | Abosolute alcohol, 23±0.5℃ |
| 7 | Flexural strength | ISO 178:2010/Amd.1:2013 Method A | Specimen：100x10.96x3.12mm |
| 8 | Flexural modulus | ||
| 9 | Charpy unnotched impact strength | ISO 179-1: 2010 | Specimen: ISO 179-1/1Eu |
| 10 | Vicat softening temperature | ISO 306:2004 Method B50 | Specimen thickness: 3.01mm Rate of temperature: 50℃/h |
| 11 | Tensile strength | ISO 527-1:2012 and ISO 527-2:2012 | Specimen: Type 1B Specimen thickness:3.05mm Testing speed: 5mm/min Grip separation:115mm |
| 12 | Nominal tensile strain at break | ||
| 13 | Impact resistance | GB/T 8814-2004 Section 5.7 and 6.7 | Precondition:-10℃，1h→ |
| 14 | Dimensional change | With reference to ASTM D1204-08 and client’s requirement | Condition: 100℃，60min→ 23±2℃，50±5%RH,1h Specimen: 25x25cm Medium: Talcum powder |
| 15 | Oxygen Index | ISO 4589-1: 1996 and ISO 4589-2: 1996/Amd.1:2005 | Specimen: Type III Specimen thickness: 3.2mm Ignition procedure: Method A |
| 16 | Horizontal burning test | UL 94-2013 Section 7 | Specimen: 126x13.4x3.0mm Conditioning: 23±2℃, 50±5%RH, 48h |
| 17 | 20mm Vertiacal burning test | UL 94-2013 Section 8 | Specimen: 126x13.4x3.0mm |
| 18 | Burning test | DIN 4102-1:1998-05 | See appendix1 |
Our Service
1. OEM Manufacturing welcome: Product, Packag...
2. Sample order
3. We will reply you for your inquiry in 24 hours.
4. after sending, we will track the products for you once every two days, until you get the products. When you got the
goods, test them, and give me a feedback.If you have any questions about the problem, contact with us, we will offer
the solve way for you
Previous: Chinese Profession
Yes, we are real manufacturer, if you need other special product, we will do our best to help you, so we can build a long-term business relationship.
Of course you can, also we will produce the products according to your detail requests.
We have direct factory and many years of export experience, and offer the best price with.high quality product, timely delivery, also have good after-sales service, therefore with good reputation on boards and with many clients have good long-term business relationship.
Payment: T/T 30% in advance, balance before shipment. Production Lead Time: Within 7 working days after 30% deposit Shipping Methods: small order will be sent by express,big order will be sent by sea.
Tel: 0086-(0)757-83128353
smartroof@fswinning.cn
Room H, 30/F, Foshan Development Building, No.13, East Hua Yuanrd, Foshan, Guangdong, China